The influence of laser surface melting and induction hardening on the surface structure,con- tact fatigue life and failure behaviour of the nodular cast iron has been investigated.The con- tact fatigue life can be improved by both laser treatment and induction hardening,but the fail- ure process and type are different from each other.The former is due to lumpy and deep spal- ling caused by crack propagation between the quenching zone and the substrate,and the latter is due to nubby and surface flaking caused by the oil wedged action into surface cracks.
关键词:
surface hardening
,
null
,
null
,
null
王韶云
,
李国禄
,
王海斗
,
刘金海
,
徐滨士
,
朴钟宇
材料热处理学报
采用超音速等离子喷涂技术在45钢基体上制备了NiCr-Cr3C2金属陶瓷涂层,使用球盘式接触疲劳试验机对涂层进行不同载荷条件下的接触疲劳试验。采用范—蒙特福特假设检验验证涂层的疲劳寿命数据,发现其符合Weibull分布,随后建立Weibull失效概率图。通过该图可以直观的得到在同一工作条件下,涂层任意循环次数的失效概率,同时可以在一定范围内,预测某一工作载荷下涂层的接触疲劳寿命。该方法在试验数据较少的情况下,较为精确的表征了涂层的接触疲劳寿命,有效的提高了试验效率,节约了试验成本。
关键词:
等离子喷涂
,
接触疲劳寿命
,
范—蒙特福特假设检验
,
Weibull分布
王韶云
,
李国禄
,
王海斗
,
刘金海
,
徐滨士
,
朴钟宇
材料热处理学报
采用超音速等离子喷涂技术在45号钢基体上制备了NiCrBSi合金涂层,随机挑选一半试样使用热处理炉进行重熔处理。使用球盘式接触疲劳试验机对涂层进行了接触疲劳试验,建立Weibull失效概率图,比较了重熔前后两种涂层接触疲劳寿命的演变规律及涂层主要的疲劳失效模式。使用扫描电子显微镜对涂层的微观结构和失效形貌进行了表征。结果表明,重熔处理能够增强涂层与基体的结合强度,提高涂层的致密度,同时使涂层的主要失效模式由分层失效转变为剥落失效,显著提高了涂层的接触疲劳寿命,降低涂层寿命的分散程度。
关键词:
等离子喷涂
,
重熔处理
,
接触疲劳寿命
,
Weibull分布
殷畅
,
张平
,
赵军军
兵器材料科学与工程
利用ZJ-Ⅱ型超声波冲击设备对20Cr2Ni4A渗碳齿轮钢进行超声冲击处理,对比研究超声冲击前后试样的接触疲劳寿命、残余应力和显微硬度随层深的变化情况.结果表明:经过超声冲击强化后,渗碳齿轮钢的接触疲劳寿命有较大幅度的提高.主要原因是晶粒细化和位错增殖抑制疲劳裂纹源的萌生,残余应力显著增加、表面硬度大幅度提高降低疲劳裂纹拓展的速率,从而使其接触疲劳性能得到显著提升.